Performance Evaluation of 3-D Basalt Fiber Reinforced Concrete & Basalt Rod Reinforced Concrete

Оценка эффективности 3D бетона, армированного базальтовой фиброй и базальтовой арматурой
Изображение: Pexels

This report presents the experimental investigation carried out to evaluate the performance characteristics of basalt fiber reinforced concrete and basalt bar reinforced concrete.

All the experiments were conducted following the ASTM standards. The test program was conducted for fresh and hardened concrete properfies. The fresh concrete properties consisted of the following tests: slump, Vebe slump, Vebe time, concrete temperature, air content and unit weight.

The hardened concrete properties determined were compressive strength, static modulus, flexural strength, load-deflection behavior, comparison of load-deflection curves, ASTM toughness indices, first crack toughness, post crack behavior, Japanese standard method for toughness indices and equivalent flexural strength.

The test results show that the basalt fiber can be easily mixed in the concrete without any balling, bridging or segregation. There was a noticeable increase in the post crack energy absorption capacity and ductility due to the addition of basalt fibers. The impact resistance increased as the fiber content increased.

Tests were also conducted on beams reinforced with basalt bars, which were supplied by the manufacturer. The load deflection curves were plotted and the toughness indices and first ciack toughness were calculated in a similar way as the ASTM standards for the beams reinforced with basalt fibers.

Toughness indices according to the Japanese Standard method and the equivalent flexural strength were also calculated. Tests were conducted on beams reinforced with basalt bars, which were designed and cast in the lab.

Strain across the depth of the beams was measured, using electrical resistance strain gauges. Deflection was measured, using a magnetic dial gauge. The tests indicated that there was insufficient bond strength and the bars slipped gradually before the ultimate load was released.

Beams with increased development lengths failed suddenly with breaking of rods. It was a sudden and brittle failure. The ultimate-load and cracking-load moments and the deflections of the basalt rod reinforced concrete beams were compared.

The tension tests were conducted on the basalt bars, and a cable, having two basalt bars twisted together. Graphs of stress vs. strain were plotted and the modulus of elasticity of the basalt bars was calculated. The fibers and bars were supplied by Research & Technology Inc., Madison, WL.

Final Report for Highway IDEA Project 45

Authors:

V. Rarnalaishnan, Neeraj S. Tolmare
South Dakota School of Mines & Technolory, Rapid City, SD
Principal Investigator: Madimir B. Brik
Research & Technology, lnc., Madison, WI